Final assignment – free form in aggregate

We set out to make an organic free form shape cast only in different sizes of aggregate.


The result of the first test of aggregate and slurry mix. The straws helped the cement mix to go down in the aggregate and the slurry mix seamed to work so we went up in size for the final cast.


We used three different sizes of aggregate, very small which we sieved, middle size and quite large pieces for where we wanted the cement mix to go down.


We poured the cement mix in steps to make sure that it would go down in the aggregate, and built the shape in many layers.

We used the slurry mix we tested in the first experiment:

750 g cement
300 g water
15 g super plasticizer


The end result.
A piece fell of in the process of removing the cast from the bucket, we could have reinforced the shape with for example steel wire, or greased the bucket before we cast.
Otherwise the shape we got was what we set out do make. The different aggregate made it possible to make voids and the shape was quite easily controlled.

How to go forward.
The method of casting in only different aggregate is good since there is not much waste material, and you don’t need that much cement since it is such a large portion of aggregate.

Final assignment – free form in aggregate

We´re trying to cast without mould using only different sizes of aggregate and letting the concrete fill the void in the bigger aggregate.


Testing two different slurrys and two different sizes of aggregate to see how far the concrete mix would go in the aggregate. Using some super plasticizer made the slurry go down more easy than using only water and cement.

Mix 1:

250 g cement

90 g water

10 g super plasticizer

Mix 2:

250 g cement

100 g water


Bigger test:

Larger aggregate in the core and finer aggregate surrounding. Making “branches” of larger aggregate from the core to see if they will be filled or not.


750 g cement

300 g water

15 g super plasicizer

We added a straw for the air in the bottom to be able to come upp when pouring in the slurry.


Assignment 05 – adaptive formwork

We worked with aluminium foil in free form. We needed to add an additional 200 g of water for the concrete mix to flow easily and get down to the bottom. The aggregate we used for the inside of the aluminium shape was perhaps to small, so the concrete didn’t get down in a good way. If we were to do it agin, we would use larger aggregate so that we wouldn’t have to use so much water.



The shape after we took it out of the form after 24 hours. There was some leakage on the top, but that rather made it more interesting. Overall the shape was kept intact.

Assignment 04 – gravity + varying stretch

When mixing the fabric-concrete, we needed to add an additional 290 g of water to a 1 kg mix in order for the concrete to flow easily.


Gravity 10×10.

We used the non-strechty fabric and placed nails on a board underneath the fabric. When adding the concrete, the load of the concrete hopefully creates a flowy landscape around the pikes of the nails.



Varying stretch 10×20.

We placed a non-stretchy fabric around a frame, made some holes and then added the strechty fabric on top. The weight of the concrete should then make deeper “valleys” of concrete where the holes in the non-stretchy fabric are.

Assignment 3 – fluid form – group 10

We used sliced baguettes in hopes that the fluid concrete would fill the air holes and cracks and pour out on the edges in spontaneous shapes. The breads holes were probably too small so the concrete didn´t sink so far into the bread. For the shape to be completely freed from the bread it will either have to dry more or be burnt off the concrete.



“Parupu” the Pulp Chair


Designed by: Claesson Koivisto Rune for Södra, 2008

Material: Pulp (Durapulp)

Process: Compressing

‘parupu’ is a chair for children, made of the material ‘durapulp’, a biodegradable plastic based on maize starch. It is durable and waterproof, as well as fully compostable. Started out as a thesis project at KTH. The project received a grant from the swedish governmental agency for innovation systems.